Gold, Platinum, Rhodium, Gold Alloys and Allergies
Gold
Gold is a dense inert bright yellow element that is the most malleable and ductile metal, occurring in rocks and alluvial deposits. The radioisotope gold-198 (radiogold), with a half-life of 2.69 days, is used in radiotherapy. Symbol: Au; atomic no.: 79; atomic weight: 196.97; valency: 1 or 3; relative density: 19.32; melting pt.: 1063°C; boiling pt.: 2966°C.
Gold and jewellery are synonymous, partly because of its use throughout history covering more than 6000 years. Its unique position of importance is not simply due to its rarity, but also its appearance and the character of the metal itself. In its pure 24 carat form its colour is a unique bright yellow which when combined with its high lustre has connected it with the sun in ancient times. Because it is practically chemically inert it does not oxidise in air and retains its high lustre.
Gold is also the most malleable and ductile of all metals and can be beaten to a transparent film approximately 0.000005mm in thickness and is used as an anti-ice and anti-mist unit when sandwiched between laminated glass in the aircraft industry.
Where does gold come from?
Practically all the gold in the world is mined. To produce one troy ounce (31.1035gms) of gold from a rich mine, about three tonnes of ore are blasted from the reefs, conveyed to the shaft, hoisted to the surface, crushed to the consistency of powder and then passed through the processes of agitation, filtration, and then treatment with potassium cyanide ( KCN a white poisonous granular soluble solid substance, much used in the jewellery trade) to separate the metal. The production of this small amount of gold requires more than 5000 litres (5 tonnes in weight) of water, 750 KWh (approx £50 in the UK at 6.5p per unit but industrially the figure is significantly less) of electricity, explosives, chemicals, compressed air and 39 man hours.
Alloys of gold
For most uses of gold the pure metal is too soft on its own and is therefore hardened by the addition of alloying elements, copper, silver, nickel, palladium and zinc. Gold is of course yellow and the various colours seen such as red, white and green are simply alloys of gold. The final colour is dependent on the ratios and type of alloys added.
Typical mixes:
9.5ct Yellow gold: gold 39.6%, silver 12.1%, copper 42.3%, zinc 6%
9.5ct white gold : gold 39.6%, silver nil% , copper 34.0%, zinc 8.7%, nickel 17.7% - (more about nickel later)
14 ct Green gold : gold 58.33%, silver 32.5%, copper 8.97%, zinc 0.2%
White Gold
Gold is yellow, copper is reddish, and all other metals are a silvery grey in colour. There are however gold alloys, that is mixes of differing metals, that appear grey/white.
White gold (alloy) became popular around 1920 as a substitute for platinum, as platinum was quite expensive. Simply mixing a white and yellow metal together will not produce a colour in the same way that mixing paint does.
The most common metal used to 'bleach' gold is nickel which is both inexpensive and provides a good platinum look-alike in 18ct alloys. It has however been linked to dermatitis through allergic reactions with the skin. It has also been suggested that it may be slightly carcinogenic. A recent E.U directive has indicated that soon all jewellry will have to be nickel safe with only a few ppm being allowable.
A typical white gold alloy might be
18ct gold 0.750, copper 0.055, nickel 0.145, zinc 0.050
A typical nickel free white alloy might be
18ct gold 0.750, copper 0.040, silver 0.040, palladium 0.170
Palladium is the next choice for use in white gold alloys and, apart from its high price and high melting point (1552 degrees celsius), is an ideal alloy. Its higher base cost and workshop recovery costs make for a more expensive product but the advantages of a non nickel alloy now out weigh these factors. Platinum, chromium, cobalt, zinc, tin and silver are all used as whiteners. Silver has excellent working properties but is poor as a whitener. Copper is also added to improve the ductility of most white alloys. It is important to remember that even the best white gold alloy is actually grey, as is platinum. The white finish you are accustomed to is a rhodium plating.
What is Rhodium Plating?
Rhodium is a hard corrosion-resistant silvery-white element of the platinum metal group, occurring free with other platinum metals in alluvial deposits and in nickel ores. It is used as an alloying agent to harden platinum and palladium. Symbol: Rh; atomic no.: 45; atomic wt.: 102.90; valency: 1-6; relative density: 12.4; melting pt.: 1966°C; boiling pt.: 3727°C (approx.).
It is usual to rhodium plate all white gold jewellery in the UK and some platinum. Rhodium is very bright, hard, and highly reflective and when applied by an electrochemical process to white gold it forms a hard white highly reflective surface to the metal. This is the polished white surface which you associate with platinum jewellery. When the rhodium plating wears through the colour of the actual alloy can be seen. This varies from a yellowish grey to a plain grey. On some cheaper jewellery, particularly 9ct, one piece castings are made from a yellow alloy. The highlights or head of a ring is later made white by 'stopping off' the yellow parts with something akin to nail varnish and rhodium plating the rest. The mask is then removed to leave the two colour item.
How long will Rhodium Plating last?
This is the 'how long is a piece of string' question. The answer depends on how thick the plating is, and how much wear the item is subjected to. An average is perhaps several years, but it can be as little as a month and we have seen rings make it beyond twenty years.
What is Platinum?
Platinum is a ductile malleable silvery-white metallic element, very resistant to heat and chemicals. It occurs free and in association with other platinum metals, especially in osmiridium: used in jewellery, laboratory apparatus, electrical contacts, dentistry, electroplating, and as a catalyst. Symbol: Pt; atomic no.: 78; atomic weight: 195.09; valency: 1-4; relative density: 21.45; melting pt.: 1772°C; boiling pt.: 3827°C (approx.).
Pure platinum works beautifully, it can be readily welded and soldered and takes a lustrous polish, but unless it is finished a heavily cold worked state, it is too soft for hardwearing jewellery. Small amounts of certain alloying elements can give platinum the properties that make it ideal for jewellery. Copper, cobalt, gold, iridium, palladium and ruthenium alloy easily with platinum.
Opinions differ on the difficulty of polishing platinum, although once well polished it maintains its finish virtually tarnish free for ever. As with any metal, the polished surface of some platinum alloys may scratch with every-day wear. Matte finish platinum tends to burnish and highly polished platinum tends to matte a little. With reasonable protection from knocks and abrasion, highly polished platinum can be brilliant and kept that way. A large proportion of platinum-palladium alloy is plated thinly with rhodium, which scarcely alters the colour but does impart some extra wear resistance.
Is 9ct harder than 18ct gold?
This is a classical myth. Actually 9ct could be harder but normally it is not. The hardness depends on many factors including both the mixture of alloys and the way the product is treated during manufacture. In general most 18ct carat alloys are both harder and more durable than their 9ct counterparts. 9ct is also usually more brittle than 18ct. If the gold is worked by rolling, hammering, bending and stretching it becomes 'work hardened'. This usually leaves the metal in a more brittle state and less suitable for wearing. By a process of heating called annealing which removes internal stress, crystal defects, and dislocations, the metal regains its former malleability. This may be carried out many times during the manufacturing of a hand made piece, but as most jewellery is cast today, this happens only once.
Do I have an allergy to gold?
Probably not, that is not gold itself. What people occasionally have is an allergy to the nickel content in gold alloys, usually in the alloy rich 9ct golds. 9ct alloys go dull or even black from the exposure to chemicals in the atmosphere and also may discolour from contact with perspiration, bleach, household chemicals and some fabrics.
Detergents and other chemicals lodge between rings and the skin causing problems, particularly hairspray, beauty and cleaning products. Antiperspirants exacerbate metal allergy problems. It has been suggested that the sweat of a healthy person after exercise contains 18 times the nickel content of blood. The antiperspirant reduces the bodies natural way of eliminating heavy metals and can lead to a build up in intensity, which causes a higher concentration in the sweat than is normal.
The most common type of allergy we encounter is a phantom allergy caused by a noticeable desire to upgrade to 18ct or platinum!.
As nickel and zinc are not used in 18ct alloy, just silver and copper, it is unlikely to produce any kind of allergy problems.
Hallmarking and Standards - Gold, Platinum and Sterling Silver
Metal: Compulsory Mark
9ct gold 375
10ct gold 416
14ct gold 585
18ct gold 750
22ct gold 916
99% pure gold 990
99.9% pure gold 999
800 grade silver 800
sterling silver 925
Britannia Silver 958
99.9% pure silver 999
85% Platinum 850
90% Platinum 900
95% (UK standard) Platinum 950
99.9% pure Platinum 999
What is Sterling Silver?
Silver is a precious metal and much like gold it is too fine to be made in a 100% form. To make it durable for jewerly, pure silver (999 fineness) is often alloyed with small quantities of copper (7.5%), thus comes sterling silver (92.5% or .925). Copper is added to strengthen the silver and make it durable to be use as a decorative or in fashionable jewerly.
How to Care for your Sterling Silver?
I take pride in my work and set high standards in the craftsmanship of our hand crafted jewelry. As with every product its life span will depend on the care you give it. These are some helpful hints on how to look after your Sterling Silver pieces.
1. To maintain the original condition of your silver jewelry, polish your pieces regularly using a non-abrasive cleaning cloth.
2. Soap and water will also help keep your silver looking good. Remember do not dry silver off with  paper towels or tissues, always use a soft cloth.
3. When you are not wearing your silver jewerly, store them in a cool, dry place. Zip-lock bag and individual cloth pouches are ideal for this and will help prevent both tarnishing or scratching by other pieces.
4. Never immerse your silver jewelry in chlorine, salt water, mineral springs, and suntan lotion. Remember, some household cleaners contain chlorine bleach, these will cause discoloration and also loosen the gemstones.
5. Avoid abrasive cleaners, detergents and commercial jewelry cleaners "dips" especially if the pieces have an oxidized finish. Using harsh polishing cleaners will alter the antique look of your jewerly.
6. Never use an ultrasonic cleaner, ammonia or any chemical solution to clean opaque gemstones, such as turquoise, malachite, onyx, lapis lazuli and opals. They are a porous stone and may absorb chemicals, which build up inside the stone and cause discoloration. Simply wipe them gently with a moist cloth until clean.
7. If your jewelry contains gemstones or pearls, do not immerse in water, as this can loosen some settings. Never use dips or abrasives cleaners on gemstones.
Ring Size
There is no substitute for having your finger measured professionally, but it's not an exact science.
Our fingers change in size from morning to evening, month to month and even Winter to Summer.
The following chart is helpful to see how the sizes are compiled.

UK: Diameter mm Circumference mm American
A 11.5 36.25 0.5
B 12.3 38.64 1
C 12.7 39.90 1.5
D 13.1 41.15 2
E 13.5 42.41 2.5
F 13.9 43.67 3
G 14.3 44.92 3.25
H 14.7 46.18 3.75
I 15.1 47.44 4.25
J 15.5 48.69 4.75
K 15.9 49.95 5.25
L 16.3 51.24 5.75
M 16.7 52.46 6.25
N 17.1 53.72 6.75
O 17.5 54.98 7
P 17.9 56.23 7.5
Q 18.3 57.49 8
R 18.7 58.75 8.5
S 19.1 60.00 9
T 19.5 61.26 9.5
U 19.9 62.52 10
V 20.3 63.77 10.5
W 20.7 65.00 11
X 21.1 66.29 11.5
Y 21.5 67.51 12
Z 21.9 68.77 12.5
Z+1 22.3 69.99
Z+2 22.7 71.31  
Z+3 23.1 72.57  
Z+4 23.5 73.83  
Z+5 23.9 75.08  
Z+6 24.3 76.34  
Z+7 24.7 77.60  
Z+8 25.1 78.86  

To calculate:
American size= (diameter-11.54)/(0.83)
Japanese size= (diameter-12.67)*3
European size= circumference-40
stones  » » » »
Copyright © 1999 - 2004 by Jack Kozielski.  All rights reserved.
E-mail:
exhibitions · about artist · galleries · jewellery · art for sale
commissions · phothography books · art movement